Nonequilibrium Statistical Modeling of Fatigue Crack Growth Behaviour

In order to study the influence of microstructural texture on the growth of short fatigue cracks in metals, the nonequilibrium statistical theory of fatigue fracture correlating a microscopic mechanism with the macroscopic properties is modified to take into consideration the microstructural features of a material, thereby allowing a rationalisation of the experimental data of short fatigue crack growth and long fatigue crack growth. The nonequilibrium statistical theory thus developed relates the growth of cracks with a dislocation mechanism to simulate short fatigue crack growth with the long fatigue crack growth behaviour and predicts the fatigue crack growth rates throughout the fatigue lifetime. The results is finally compared with that of other fatigue theories.